  • Thumbnail Image
    ItemOpen Access
    Effects of milling and annealing on formation and structural characterization of nanocrystalline intermetallic compounds from Ni-Ti elemental powders
    (2012) Ghadimi, M.; Shokuhfar, A.; Rostami H.R.; Ghaffari, M.
    Nickel and Titanium elemental powders with a nominal composition Ni-50 at.%Ti were mechanical alloyed in a planetary high-energy ball mill in different milling conditions (5, 10, 20, 40 and 60 h). The investigation revealed that increasing milling time leads to a reduction in crystallite size, and after 60 h of milling, the Ti dissolved in Ni lattice and NiTi (B2) phase was obtained. With milling time, morphology of pre-alloyed powders changed from lamella to globular. Annealing of as-milled powders at 1173 K for 900 s led to formation of nanocrystalline NiTi (B19′), grain growth and release of internal strain. The results indicated that this technique is a powerful and high productive process for preparing NiTi intermetallic compound with nanocrystalline structure and appropriate morphology. © 2012 Elsevier B.V. All rights reserved.
  • Thumbnail Image
    ItemOpen Access
    Liquid-phase sintering of medical-grade P558 stainless steel using a new biocompatible eutectic additive
    (Elsevier, 2012-02-02) Salahinejad, E.; Hadianfard, M. J.; Ghaffari, M.; Mashhadi, S. B.; Okyay, Ali Kemal
    One of the effective approaches to reduce residual pores in powder metallurgy parts is activated liquid-phase sintering process using proper additives. In this work, for the first time, a new biocompatible additive (Mn-11.5 wt.% Si, a eutectic alloy) is experimented for liquid-phase sintering of nanocrystalline/amorphous P558 stainless steel powders. It is realized that by increasing the sintering aid content and temperature, the density is effectively increased: a sharp densification progress when the sintering temperature increases from 1000 °C to 1050 °C and a slower densification rate when it exceeds 1050 °C. This preliminary study opens up the development of high-density medical-grade stainless steels produced by powder metallurgy, where suitable additives can lower sintering temperature and time, which is promising for retarding grain growth and commercial applications.
  • Thumbnail Image
    ItemOpen Access
    Microstructural characterization of medical-grade stainless steel powders prepared by mechanical alloying and subsequent annealing
    (Elsevier, 2013) Salahinejad, E.; Hadianfard, M. J.; Ghaffari, M.; Amini, R.; Mashhadi, S. B.; Okyay, Ali Kemal
    The harmful effect of nickel ions released from conventional stainless steel implants has provided a high level of motivation for the further development of nickel-free stainless steels. In this paper, the microstructure of medical-grade nickel-free stainless steel powders, with the chemical composition of ASTM F2581, is studied during mechanical alloying and subsequent annealing. Rietveld X-ray diffraction and transmission electron microscopy evaluations reflect nanocrystallization, austenitization and amorphization of the powders due to mechanical activation. It is also realized that annealing of the as-milled powder can develop a single austenitic structure with nanometric crystallite sizes, implying a considerable inherent resistance to grain growth. This study demonstrates the merit of mechanical alloying and subsequent annealing in the development of nanostructured medical-grade stainless steels.