  • Thumbnail Image
    ItemOpen Access
    Antibacterial electrospun nanofibers from triclosan/cyclodextrin inclusion complexes
    (Elsevier, 2014) Celebioglu A.; Umu, O. C. O.; Tekinay, T.; Uyar, Tamer
    The electrospinning of nanofibers (NF) from cyclodextrin inclusion complexes (CD-IC) with an antibacterial agent (triclosan) was achieved without using any carrier polymeric matrix. Polymer-free triclosan/CD-IC NF were electrospun from highly concentrated (160% CD, w/w) aqueous triclosan/CD-IC suspension by using two types of chemically modified CD; hydroxypropyl-beta-cyclodextrin (HPβCD) and hydroxypropyl-gamma-cyclodextrin (HPγCD). The morphological characterization of the electrospun triclosan/CD-IC NF by SEM elucidated that the triclosan/HPβCD-IC NF and triclosan/HPγCD-IC NF were bead-free having average fiber diameter of 520±250nm and 1100±660nm, respectively. The presence of triclosan and the formation of triclosan/CD-IC within the fiber structure were confirmed by 1H-NMR, FTIR, XRD, DSC, and TGA studies. The initial 1:1molar ratio of the triclosan:CD was kept for triclosan/HPβCD-IC NF after the electrospinning and whereas 0.7:1molar ratio was observed for triclosan/HPγCD-IC NF and some uncomplexed triclosan was detected suggesting that the complexation efficiency of triclosan with HPγCD was lower than that of HPβCD. The antibacterial properties of triclosan/CD-IC NF were tested against Gram-negative (Escherichia coli) and Gram-positive (Staphylococcus aureus) bacteria. It was observed that triclosan/HPβCD-IC NF and triclosan/HPγCD-IC NF showed better antibacterial activity against both bacteria compared to uncomplexed pure triclosan.
  • Thumbnail Image
    ItemOpen Access
    Surface-modified bacterial nanofibrillar PHB scaffolds for bladder tissue repair
    (Taylor and Francis Ltd., 2016) Karahaliloǧlu, Z.; Demirbilek, M.; Şam, M.; Saǧlam, N.; Mizrak, A. K.; Denkbaş, E. B.
    The aim of the study is in vitro investigation of the feasibility of surface-modified bacterial nanofibrous poly [(R)-3-hydroxybutyrate] (PHB) graft for bladder reconstruction. In this study, the surface of electrospun bacterial PHB was modified with PEG- or EDA via radio frequency glow discharge method. After plasma modification, contact angle of EDA-modified PHB scaffolds decreased from 110 � 1.50 to 23 � 0.5 degree. Interestingly, less calcium oxalate stone deposition was observed on modified PHB scaffolds compared to that of non-modified group. Results of this study show that surface-modified scaffolds not only inhibited calcium oxalate growth but also enhanced the uroepithelial cell viability and proliferation.
  • Thumbnail Image
    ItemOpen Access
    Uptake of Ba2+ ions by natural bentonite and CaCO3: a radiotracer, EDXRF and PXRD study
    (Akademiai Kiado Rt., 2002) Shahwan, T.; Atesin, A. C.; Erten, H. N.; Zararsiz, A.
    Ba2+ uptake by natural bentonite, CaCO3 in addition to a number of bentonite-CaCO3 mixtures with variable compositions as a function of pH and Ba2+ concentration was studied. Radiotracer method, EDXRF, and PXRD were used. The results of radiotracer experiments showed that the uptake of Ba2+ by CaCO3 was larger than its uptake by natural bentonite samples, particularly at low initial concentrations of Ba2+ and higher pH values. This finding was supported by the EDXRF results, According to the sorption data, the apparent ΔG° values of sorption were in the range -9±1 to -13±3 kJ/mol. The PXRD studies revealed the formation of BaCO3 upon sorption of Ba2+ on pure CaCO3 and on some of the bentonite-CaCO3 mixtures.