Nanohybrid structured RuO2/Mn2O3/CNF as a catalyst for Na-O2 batteries

Series

Abstract

A 3D RuO2/Mn2O3/carbon nanofiber (CNF) composite has been prepared in this study by a facile two step microwave synthesis, as a bi-functional electrocatalyst towards oxygen reduction reaction (ORR) and oxygen evolution reaction (OER). RuO2 nanoparticles with the mean size of 1.57 nm are uniformly distributed on Mn2O3 nano-rods grown on electrospun CNFs. The electrocatalytic activity of the composites are investigated towards ORR/OER under alkaline condition. The ternary RuO2/Mn2O3/CNF composite showed superior ORR activity in terms of onset potential (0.95 V versus RHE) and Tafel slope (121 mV dec-1) compared to its RuO2/CNF and Mn2O3/CNF counterparts. In the case of OER, the RuO2/Mn2O3/CNF exhibited 0.34 V over-potential value measured at 10 mA cm-2 and 52 mV dec-1 Tafel slope which are lower than those of the other synthesized samples and as compared to state of the art RuO2 and IrO x type materials. RuO2/Mn2O3/CNF also exhibited higher specific capacity (9352 mAh ) than CNF (1395 mAh ), Mn2O3/CNF (3108 mAh ) and RuO2/CNF (4859 mAh g carbon -1) as the cathode material in Na-O2 battery, which indicates the validity of the results in non-aqueous medium. Taking the benefit of RuO2 and Mn2O3 synergistic effect, the decomposition of inevitable side products at the end of charge occurs at 3.838 V versus Na/Na+ by using RuO2/Mn2O3/CNF, which is 388 mV more cathodic compared with CNF.

Source Title

Nanotechnology

Publisher

Institute of Physics Publishing

Course

Other identifiers

Book Title

Degree Discipline

Degree Level

Degree Name

Citation

Published Version (Please cite this version)

Language

English