Browsing by Subject "TEM images"
Now showing 1 - 3 of 3
Results Per Page
Sort Options
Item Open Access Carbon supported nano-sized Pt-Pd and Pt-Co electrocatalysts for proton exchange membrane fuel cells(2009) Kadirgan, F.; Kannan, A. M.; Atilan, T.; Beyhan, S.; Ozenler, S. S.; Süzer, Şefik; Yörür, A.Nano-sized Pt-Pd/C and Pt-Co/C electrocatalysts have been synthesized and characterized by an alcohol-reduction process using ethylene glycol as the solvent and Vulcan XC-72R as the supporting material. While the Pt-Pd/C electrodes were compared with Pt/C (20 wt.% E-TEK) in terms of electrocatalytic activity towards oxidation of H2, CO and H2-CO mixtures, the Pt-Co/C electrodes were evaluated towards oxygen reduction reaction (ORR) and compared with Pt/C (20 wt.% E-TEK) and Pt-Co/C (20 wt.% E-TEK) and Pt/C (46 wt.% TKK) in a single cell. In addition, the Pt-Pd/C and Pt-Co/C electrocatalyst samples were characterized by XRD, XPS, TEM and electroanalytical methods. The TEM images of the carbon supported platinum alloy electrocatalysts show homogenous catalyst distribution with a particle size of about 3-4 nm. It was found that while the Pt-Pd/C electrocatalyst has superior CO tolerance compared to commercial catalyst, Pt-Co/C synthesized by polyol method has shown better activity and stability up to 60 °C compared to commercial catalysts. Single cell tests using the alloy catalysts coated on Nafion-212 membranes with H2 and O2 gases showed that the fuel cell performance in the activation and the ohmic regions are almost similar comparing conventional electrodes to Pt-Pd anode electrodes. However, conventional electrodes give a better performance in the ohmic region comparing to Pt-Co cathode. It is worth mentioning that these catalysts are less expensive compared to the commercial catalysts if only the platinum contents were considered.Item Open Access Facile synthesis of cross-linked patchy fluorescent conjugated polymer nanoparticles by click reactions(2011) İbrahimova, V.; Ekiz, S.; Gezici, Ö.; Tuncel, D.Here, we report a novel method to synthesize multifunctional nanoparticles that can be used in biological studies, such as in cell imaging and as a carrier for biomolecules/drugs. The nanoparticles were prepared either via Cu-catalyzed or cucurbit[6]uril (CB6)-catalyzed click reactions between azide groups containing hydrophobic blue, green and yellow emitting fluorene-based conjugated polymers and a hydrophilic diaminodialkyne containing cross-linker. Through the click reaction, not only does the cross-linking confer stability, but it also introduces functional groups, such as triazoles and amines, to the nanoparticles. Moreover, CB6 not only acted as a catalyst to facilitate the copper-free click reaction, but it also allowed us to obtain nanoparticles containing rotaxanes in which the triazole units were encapsulated by CB6 units. TEM images of the nanoparticles also showed that they display very interesting morphologies. Incorporation of hydrophilic functional groups to the hydrophobic conjugated polymers resulted in a distinct phase separation, producing Janus-like or patchy particles.Item Open Access Preparation of Al 2O 3and AlN nanotubes by atomic layer deposition(Cambridge University Press, 2012) Ozgit-Akgun, Çagla; Kayacı, Fatma; Dönmez, İnci; Çağatay, Engin; Uyar, Tamer; Bıyıklı, NecmiAl 2O 3 and AlN nanotubes were fabricated by depositing conformal thin films via atomic layer deposition (ALD) on electrospun nylon 66 (PA66) nanofiber templates. Depositions were carried out at 200°C, using trimethylaluminum (TMAl), water (H 2O), and ammonia (NH 3) as the aluminum, oxygen, and nitrogen precursors, respectively. Deposition rates of Al 2O 3 and AlN at this temperature were ∼1.05 and 0.86 Å/cycle. After the depositions, Al 2O 3- and AlN-coated nanofibers were calcinated at 500°C for 2 h in order to remove organic components. Nanotubes were characterized by using X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). AlN nanotubes were polycrystalline as determined by high resolution TEM (HR-TEM) and selected area electron diffraction (SAED). TEM images of all the samples reported in this study indicated uniform wall thicknesses. © 2012 Materials Research Society.