  • Thumbnail Image
    ItemOpen Access
    High quantum efficiency Type-II superlattice N-structure photodetectors with thin intrinsic layers
    (SPIE, 2013) Ergun, Y.; Hostut, M.; Tansel, T.; Muti, bdullah; Kilic, A.; Turan, R.; Aydınlı, Atilla
    We report on the development of InAs/AlSb/GaSb based N-structure superlattice pin photodiode. In this new design, AlSb layer in between InAs and GaSb layers acts as an electron barrier that pushes electron and hole wave functions towards the GaSb/InAs interface to perform strong overlap under reverse bias. Experimental results show that, with only 20 periods of intrinsic layers, dark current density and dynamic resistance at -50 mV bias are measured as 6×10-3 A/cm2 and 148 ωcm2 at 77K, respectively. Under zero bias, high spectral response of 1.2A/W is obtained at 5 μm with 50% cut-off wavelengths (λc) of 6 μm. With this new design, devices with only 146 nm thick i-regions exhibit a quantum efficiency of 42% at 3 μm with front-side illimunation and no anti-reflection coatings. © 2013 SPIE.
  • Thumbnail Image
    ItemOpen Access
    Low-frequency noise behavior at reverse bias region in InAs/GaSb superlattice photodiodes on mid-wave infrared
    (SPIE, 2013) Tansel, T.; Kutluer, K.; Muti, Abdullah; Salihoğlu, Ömer; Aydınlı, Atilla; Turan, R.
    We describe a relationship between the noise characterization and activation energy of InAs/GaSb superlattice Mid- Wavelength-Infrared photodiodes for different passivation materials applied to the device. The noise measurements exhibited a frequency dependent plateau (i.e. 1/f-noise characteristic) for unpassivated as well as Si3N4 passivated samples whereas 1/f-type low noise suppression (i.e. frequency independent plateau) with a noise current reduction of more than one order of magnitude was observed for SiO2 passivation. For reverse bias values below -0.15V, the classical Schottky-noise calculation alone did not appear to describe the noise mechanism in a SL noise behavior, which shows a divergence between theoretically and experimentally determined noise values. We identify that, the additional noise appears, with and without passivation, at the surface activation energy of < 60 meV and is inversely proportional to the reverse bias. This is believed to be caused by the surface dangling-bonds (as well as surface states) whose response is controlled by the applied reverse bias. The calculated noise characteristics showed a good agreement with the experimental data. © 2013 SPIE.