  • Thumbnail Image
    ItemOpen Access
    High-performance solar-blind AlGaN photodetectors
    (SPIE, 2005) Özbay, Ekmel; Tut, Turgut; Bıyıklı, N.
    Design, fabrication, and characterization of high-performance Al xGa1-xN-based photodetectors for solar-blind applications are reported. AlxGa1-xN heterostructures were designed for Schottky, p-i-n, and metal-semiconductor-metal (MSM) photodiodes. The solar-blind photodiode samples were fabricated using a microwave compatible fabrication process. The resulting devices exhibited extremely low dark currents. Below 3 fA leakage currents at 6 V and 12 V reverse bias were measured on p-i-n and Schottky photodiode samples respectively. The excellent current-voltage (I-V) characteristics led to a detectivity performance of 4.9×1014 cmHz1/2W-1. The MSM devices exhibited photoconductive gain, while Schottky and p-i-n samples displayed 0.15 A/W and 0.11 A/W peak responsivity values at 267 nm and 261 nm respectively. All samples displayed true solar-blind response with cut-off wavelengths smaller than 280 nm. A visible rejection of 4×104 was achieved with Schottky detector samples. High speed measurements at 267 nm resulted in fast pulse responses with >GHz bandwidths. The fastest devices were MSM photodiodes with a maximum 3-dB bandwidth of 5.4 GHz.
  • Thumbnail Image
    ItemOpen Access
    High-performance solar-blind photodetectors based on AlxGa 1_xN heterostructures
    (IEEE, 2004) Özbay, Ekmel; Bıyıklı, Necmi; Kimukin, I.; Kartaloglu, T.; Tut, T.; Aytür, O.
    Design, fabrication, and characterization of high-performance AI xGa1-xN-based photodetectors for solar-blind applications are reported. AlxGa1-xN heterostructures were designed for Schottky. p-i-n, and metal-semicondnctor-metal (MSM) photodiodes. The solar-blind photodiode samples were fabricated using a microwave compatible fabrication process. The resulting devices exhibited extremely low dark currents. Below 3 fA, leakage currents at 6-V reverse bias were measured on p-i-n samples. The excellent current-voltage (I-V) characteristics led to a detectivity performance of 4.9×1014 cmHz1/2W -1. The MSM devices exhibited photoconductive gain, while Schottky and p-i-n samples displayed 0.09 and 0.11 A/W peak responsivity values at 267 and 261 nm, respectively. A visible rejection of 2×104 was achieved with Schottky samples. High-speed measurements at 267 nm resulted in fast pulse responses with greater than gigahertz bandwidths. The fastest devices were MSM photodiodes with a maximum 3-dB bandwidth of 5.4 GHz.