    Characterization of AlInN/AlN/GaN heterostructures with different AlN buffer thickness
    (Springer New York LLC, 2016) Çörekçi, S.; Dugan, S.; Öztürk, M. K.; Çetin, S. Ş.; Çakmak, M.; Özçelik, S.; Özbay, Ekmel
    Two AlInN/AlN/GaN heterostructures with 280-nm- and 400-nm-thick AlN buffer grown on sapphire substrates by metal-organic chemical vapor deposition (MOCVD) have been investigated by x-ray diffraction (XRD), atomic force microscopy (AFM), photoluminescence (PL) and Hall-effect measurements. The symmetric (0002) plane with respect to the asymmetric (101 ¯ 2) plane in the 280-nm-thick AlN buffer has a higher crystal quality, as opposed to the 400-nm-thick buffer. The thinner buffer improves the crystallinity of both (0002) and (101 ¯ 2) planes in the GaN layers, it also provides a sizeable reduction in dislocation density of GaN. Furthermore, the lower buffer thickness leads to a good quality surface with an rms roughness of 0.30 nm and a dark spot density of 4.0 × 108 cm−2. The optical and transport properties of the AlInN/AlN/GaN structure with the relatively thin buffer are compatible with the enhancement in its structural quality, as verified by XRD and AFM results.
  • Thumbnail Image
    ItemOpen Access
    Controlled growth and characterization of epitaxially-laterally-overgrown InGaN/GaN quantum heterostructures
    (IEEE, 2010) Sarı, Emre; Akyuz, Özgün; Choi, E. -G.; Lee I.-H.; Baek J.H.; Demir, Hilmi Volkan
    Crystal material quality is fundamentally important for optoelectronic devices including laser diodes and light emitting diodes. To this end epitaxial lateral overgrowth (ELO) has proven to be a powerful technique for reducing dislocation density in GaN and its alloys [1,2]. Implementation and design of ELO process is, however, critical for obtaining high-quality material with high-efficiency quantum structures for light emitters [3]. ©2010 IEEE.
  • Thumbnail Image
    ItemOpen Access
    Examination of the temperature related structural defects of InGaN/GaN solar cells
    (Academic Press, 2015) Durukan, İ. K.; Bayal, Ö.; Kurtuluş, G.; Baş, Y.; Gültekin, A.; Öztürk, M. K.; Çörekçi, S.; Tamer, M.; Özçelik, S.; Özbay, Ekmel
    In this study the effects of the annealing temperature on the InGaN/GaN solar cells with different In-contents grown on sapphire substrate by the Metal Organic Chemical Vapor Deposition (MOCVD) are analyzed by High Resolution X-ray Diffraction (HRXRD) and an Atomic Force Microscope (AFM). The plane angles, mosaic crystal sizes, mixed stress, dislocation intensities of the structure of the GaN and InGaN layers are determined. According to the test results, there are no general characteristic trends observed due to temperature at both structures. There are fluctuating failures determined at both structures as of 350 °C. The defect density increased on the GaN layer starting from 350 °C and reaching above 400 °C. A similar trend is observed on the InGaN layer, too.