Browsing by Subject "C-plane sapphire substrates"
Now showing 1 - 2 of 2
Results Per Page
Sort Options
Item Open Access Electric field dependence of radiative recombination lifetimes in polar InGaN/GaN quantum heterostructures(IEEE, 2009) Sarı, Emre; Nizamoğlu, Sedat; Lee I.-H.; Baek J.-H.; Demir, Hilmi VolkanWe report on external electric field dependence of recombination lifetimes in polar InGaN/GaN quantum heterostructures. In our study, we apply external electric fields one order of magnitude less than and in opposite direction to the polarization-induced electrostatic fields inside the well layers. Under the increasing external electric field, we observe a decrease in carrier lifetimes (τ) and radiative recombination lifetimes (τr), latter showing a weaker dependence. Our results on τr show an agreement with our transfer matrix method based simulation results and demonstrate Fermi's golden rule in polar InGaN/GaN quantum heterostructures dependent on electric field. For our study, we grew 5 pairs of 2.5 nm thick In0.15Ga 0.85N quantum well and 7.5 nm thick GaN barrier layers in a p-i-n diode architecture using metal-organic chemical vapor deposition (MOCVD) on a c-plane sapphire substrate. Devices with 300 μm × 300 μm mesa size were fabricated using standard photolithography, reactive ion etching and metallization steps. We used indium-tin oxide (ITO) based semi-transparent contacts in top (p-GaN) layer for uniform application of electric field across the well layers. The fabricated devices were diced and mounted on a TO-can for compact testing. © 2009 IEEE.Item Open Access Substrate impact on the low-temperature growth of GaN thin films by plasma-assisted atomic layer deposition(AVS Science and Technology Society, 2016) Kizir, S.; Haider, A.; Bıyıklı, NecmiGallium nitride (GaN) thin films were grown on Si (100), Si (111), and c-plane sapphire substrates at 200 �C via hollow-cathode plasma-assisted atomic layer deposition (HCPA-ALD) using GaEt3 and N2/H2 plasma as group-III and V precursors, respectively. The main aim of the study was to investigate the impact of substrate on the material properties of low-temperature ALD-grown GaN layers. Structural, chemical, and optical characterizations were carried out in order to evaluate and compare film quality of GaN on different substrates. X-ray reflectivity measurements showed film density values of 5.70, 5.74, and 5.54 g/cm3 for GaN grown on Si (100), Si (111), and sapphire, respectively. Grazing incidence x-ray diffraction measurements exhibited hexagonal wurtzite structure in all HCPA-ALD grown GaN samples. However, dominant diffraction peak for GaN films grown on Si and sapphire substrates were detected differently as (002) and (103), respectively. X-ray diffraction gonio scans measured from GaN grown on c-plane sapphire primarily showed (002) orientation. All samples exhibited similar refractive index values (∼2.17 at 632 nm) with 2-3 at. % of oxygen impurity existing within the bulk of the films. The grain size was calculated as ∼9-10 nm for GaN grown on Si (100) and Si (111) samples while it was ∼5 nm for GaN/sapphire sample. Root-mean-square surface roughness values found as 0.68, 0.76, and 1.83 nm for GaN deposited on Si (100), Si (111), and sapphire, respectively. Another significant difference observed between the samples was the film growth per cycle: GaN/sapphire sample showed a considerable higher thickness value when compared with GaN/Si samples, which might be attributed to a possibly more-efficient nitridation and faster nucleation of sapphire surface.