Browsing by Subject "Two-dimensional electron gas (2DEG)"
Now showing 1 - 2 of 2
Results Per Page
Sort Options
Item Open Access Analysis of defect related optical transitions in biased AlGaN/GaN heterostructures(2010) Bengi, A.; Lisesivdin, S.B.; Kasap, M.; Mammadov, T.; Ozcelik, S.; Özbay, EkmelThe optical transitions in AlGaN/GaN heterostructures that are grown by metalorganic chemical vapor deposition (MOCVD) have been investigated in detail by using Hall and room temperature (RT) photoluminescence (PL) measurements. The Hall measurements show that there is two-dimensional electron gas (2DEG) conduction at the AlGaN/GaN heterointerface. PL measurements show that in addition to the characteristic near-band edge (BE) transition, there are blue (BL) and yellow luminescence (YL) bands, free-exciton transition (FE), and a neighboring emission band (NEB). To analyze these transitions in detail, the PL measurements were taken under bias where the applied electric field changed from 0 to 50 V/cm. Due to the applied electric field, band bending occurs and NEB separates into two different peaks as an ultraviolet luminescence (UVL) and Y4 band. Among these bands, only the yellow band is unaffected with the applied electric field. The luminescence intensity change of these bands with an electric field is investigated in detail. As a result, the most probable candidate of the intensity decrease with an increasing electric field is the reduction in the radiative lifetime. © 2010 Elsevier Ltd. All rights reserved.Item Open Access Mobility limiting scattering mechanisms in nitride-based two-dimensional heterostructures with the InGaN channel(IOP Publishing, 2010-03-16) Gökden, S.; Tülek, R.; Teke, A.; Leach, J. H.; Fan, Q.; Xie, J.; Özgür, Ü.; Morkoç, H.; Lisesivdin, S. B.; Özbay, EkmelThe scattering mechanisms limiting the carrier mobility in AlInN/AlN/InGaN/GaN two-dimensional electron gas (2DEG) heterostructures were investigated and compared with devices without InGaN channel. Although it is expected that InGaN will lead to relatively higher electron mobilities than GaN, Hall mobilities were measured to be much lower for samples with InGaN channels as compared to GaN. To investigate these observations the major scattering processes including acoustic and optical phonons, ionized impurity, interface roughness, dislocation and alloy disorder were applied to the temperature-dependent mobility data. It was found that scattering due mainly to interface roughness limits the electron mobility at low and intermediate temperatures for samples having InGaN channels. The room temperature electron mobilities which were determined by a combination of both optical phonon and interface roughness scattering were measured between 630 and 910 cm2 (V s)-1 with corresponding sheet carrier densities of 2.3-1.3 × 1013 cm-2. On the other hand, electron mobilities were mainly limited by intrinsic scattering processes such as acoustic and optical phonons over the whole temperature range for Al0.82In 0.18N/AlN/GaN and Al0.3Ga0.7N/AlN/GaN heterostructures where the room temperature electron mobilities were found to be 1630 and 1573 cm2 (V s)-1 with corresponding sheet carrier densities of 1.3 and 1.1 × 1013 cm-2, respectively. By these analyses, it could be concluded that the interfaces of HEMT structures with the InGaN channel layer are not as good as that of a conventional GaN channel where either AlGaN or AlInN barriers are used. It could also be pointed out that as the In content in the AlInN barrier layer increases the interface becomes smoother resulted in higher electron mobility.