Browsing by Subject "Synthesized materials"
Now showing 1 - 3 of 3
Results Per Page
Sort Options
Item Open Access Cucurbit [7] uril-threaded fluorene-thiophene-based conjugated polyrotaxanes(Royal Society of Chemistry, 2016) Idris, M.; Bazzar, M.; Guzelturk, B.; Demir, Hilmi Volkan; Tuncel, D.Here we investigate the effect of cucurbit[7]uril (CB7) on the thermal and optical properties of fluorene-thiophene based conjugated polyelectrolytes. For this purpose, poly(9,9′-bis(6′′-(N,N,N-trimethylammonium)hexyl)fluorene-alt-co-thiophenelene) P1 and poly(9,9′-bis(6′′-(N,N,N-trimethylammonium)propyl)fluorene-alt-co-thiophenelene) P2 and their CB7-based polyrotaxane counterparts, P1CB7 and P2CB7, are synthesized by threading the part of the conjugated backbone of these polymers with CB7 during their synthesis. Threading efficiency in the P1CB7 containing hexyl pendant of as high as 50% is achieved, but in the case of P2, with the propyl pendant, only around 15% is achieved. We observed significant changes in the optical properties of both P1CB7 and P2CB7 with respect to their polymers P1 and P2. Fluorescent quantum yields of P1 and P2 which are 0.11 and 0.35 have increased to 0.46 and 0.55 for P1CB7 (>4 fold) and P2CB7, respectively. Moreover, polyrotaxanes compared to their polymers exhibit longer fluorescence lifetimes in the solution and the solid state thanks to the suppressed overall nonradiative recombination via encapsulation of the conjugated polymer backbone. Thermal analysis also indicates that polyrotaxanes have higher thermal stabilities than their polymer counterparts. In order to demonstrate the applicability of the synthesized materials, we also fabricated proof-of-concept light emitting diodes from P1 and its CB7-based polyrotaxane counterpart P1CB7. The CB7-integrating polymer showed lower turn-on voltages with high electroluminescence colour purity due to balanced charge injection in P1CB7 as compared to the P1 polymer.Item Open Access Fast and quick degradation properties of doped and capped ZnO nanoparticles under UV-Visible light radiations(Elsevier Ltd, 2016) Mittal, M.; Sharma, M.; Pandey, O. P.Undoped and Manganese (Mn) doped zinc oxide (ZnO) (Zn1- xMnxO, x=0.005, 0.01, 0.015 and 0.02) nanoparticles (NPs) capped with (1.0%) Thioglycerol (TG) has been successfully synthesized by co-precipitation method. Optical and morphological studies have been done for photophysical and structural analysis of synthesized materials. The photocatalytic activity of undoped and Mn doped ZnO NPs were investigated by degradation of crystal violet (CV) dye under UV-Visible light radiations. It has been found that Mn (1.0%) doping concentration is optimal for photophysical and photocatalytic properties. When the pH of as synthesized optimum doped ZnO NPs varied from natural pH i.e. from 6.7 to 8.0 and 10.0, the degradation of CV dye increases from 92% to 95% and 98% in 180min respectively. Further on increasing the pH of optimum doped synthesized NPs to 12.0, almost 100% degradation has been achieved in 150min. Optimum doped photocatalyst synthesized at pH-12.0 has also effectively degraded the CV dye solution in acidic and basic medium thus showed its utility in various industries. However, it has been found that 100% of CV dye quickly degraded in 30min when only 1.0% of hydrogen peroxide (H2O2) was introduced along with optimized NPs synthesized at pH-12. Kinetic studies show that the degradation of CV dye follows pseudo first and second-order kinetic law. Further an industrial anionic polyazo Sirius red F3B (SRF3B) dye has been degraded to 100% with optimized NPs synthesized at pH-12.0 in 15min only.Item Open Access Fe promoted NOx storage materials: structural properties and NOx uptake(American Chemical Society, 2010) Kayhan, E.; Andonova, S. M.; Şentürk, G. S.; Chusuei, C. C.; Ozensoy, E.Fe promoted NOx storage materials were synthesized in the form of FeOx/BaO/Al2O3 ternary oxides with varying BaO (8 and 20 wt %) and Fe (5 and 10 wt %) contents. Synthesized NOx storage materials were investigated via TEM, EELS, BET, FTIR, TPD, XRD, XPS, and Raman spectroscopy, and the results were compared with the conventional BaO/Al2O3 NOx storage system. Our results suggest that the introduction of Fe in the BaO/Al2O3 system leads to the formation of additional NOx storage sites which store NOx mostly in the form of bidentate nitrates. NO2 adsorption experiments at 323 K via FTIR indicate that, particularly in the early stages of the NOx uptake, the NOx storage mechanism is significantly altered in the presence of Fe sites where a set of new surface nitrosyl and nitrite groups were detected on the Fe sites and the surface oxidation of nitrites to nitrates is significantly hindered with respect to the BaO/Al2O3 system. Evidence for the existence of both Fe3+ as well as reduced Fe2+/(3-x)+ sites on the freshly pretreated materials was detected via EELS, FTIR, Raman, and XRD experiments. The influence of the Fe sites on the structural properties of the synthesized materials was also studied by performing ex situ annealing protocols within 323-1273 K followed by XRD and Raman experiments where the temperature dependent changes in the morphology and the composition of the surface domains were analyzed in detail. On the basis of the TPD data, it was found that the relative stability of the stored NOx species is influenced by the morphology of the Ba and Fe containing NOx-storage domains. The relative stabilities of the investigated NOx species were found to increase in the following order: N2O3/NO+ < nitrates on γ-Al2O3 < surface nitrates on BaO < bidentate nitrates on FeOx sites < bulk nitrates on BaO.