Browsing by Subject "Osteoblast"

Now showing 1 - 2 of 2

Open Access
Antibacterial properties and osteoblast interactions of microfluidically synthesized chitosan – SPION composite nanoparticles
(Wiley Periodicals LLC, 2023-05-26) Kafali, M.; Şahinoğlu, O. Berkay; Tufan, Y.; Orsel, Z. C.; Aygun, Elif; Alyuz, Beril; Saritas, Emine Ulku; Erdem, E. Yegan; Ercan, B.
In this research, a multi-step microfluidic reactor was used to fabricate chitosan – superparamagnetic iron oxide composite nanoparticles (Ch – SPIONs), where composite formation using chitosan was aimed to provide antibacterial property and nanoparticle stability for magnetic resonance imaging (MRI). Monodispersed Ch – SPIONs had an average particle size of 8.8 ± 1.2 nm with a magnetization value of 32.0 emu/g. Ch – SPIONs could be used as an MRI contrast agent by shortening T2 relaxation parameter of the surrounding environment, as measured on a 3 T MRI scanner. In addition, Ch – SPIONs with concentrations less than 1 g/L promoted bone cell (osteoblast) viability up to 7 days of culture in vitro in the presence of 0.4 T external static magnetic field. These nanoparticles were also tested against Staphylococcus aureus (S. aureus) and Pseudomonas aeruginosa (P. aeruginosa), which are dangerous pathogens that cause infection in tissues and biomedical devices. Upon interaction of Ch – SPIONs with S. aureus and P. aeruginosa at 0.01 g/L concentration, nearly a 2-fold reduction in the number of colonies was observed for both bacteria strains at 48 h of culture. Results cumulatively showed that Ch – SPIONs were potential candidates as a cytocompatible and antibacterial agent that can be targeted to biofilm and imaged using an MRI.
Open Access
Chemical and topographical modification of PHBV surface to promote osteoblast alignment and confinement
(John Wiley & Sons, Inc., 2008) Kenar, H.; Kocabas, A.; Aydınlı, Atilla; Hasirci, V.
Proper cell attachment and distribution, and thus stronger association in vivo between a bone implant and native tissue will improve the success of the implant. In this study, the aim was to achieve promotion of attachment and uniform distribution of rat mesenchymal stem cell-derived osteoblasts by introducing chemical and topographical cues on poly(3-hydroxybutyrate-co-3- hydroxyvalerate) (PHBV) film surfaces. As the chemical cues, either alkaline phosphatase was covalently immobilized on the film surface to induce deposition of calcium phosphate minerals or fibrinogen was adsorbed to improve cell adhesion. Microgrooves and micropits were introduced on the film surface by negative replication of micropatterned Si wafers. Both chemical cues improved cell attachment and even distribution on the PHBV films, but Fb was more effective especially when combined with the micropatterns. Cell alignment (<10° deviation angle) parallel to chemically modified microgrooves (1, 3, or 8 μm groove width) and on 10 μm-thick Fb lines printed on the unpatterned films was achieved. The cells on unpatterned and 5 μm-deep micropitted films were distributed and oriented randomly. Results of this study proved that microtopographies on PHBV can improve osseointegration when combined with chemical cues, and that microgrooves and cell adhesive protein lines on PHBV can guide selective osteoblast adhesion and alignment.