Browsing by Subject "Homogeneous distribution"

Now showing 1 - 2 of 2

Open Access
Polyhedral oligomeric silsesquioxane-based hybrid networks obtained via thiol-epoxy click chemistry
(Springer, 2017) Bekin Acar, S.; Ozcelik, M.; Uyar, Tamer; Tasdelen, M. A.
A series of hybrid networks based on polyhedral oligomeric silsesquioxane (POSS) were prepared by thiol-epoxy click reaction using commercially available octakis-glycidyl-POSS (G-POSS), trimethylolpropane triglycidyl ether, and trimethylolpropane tris(3-mercaptopropionate) as monomers. The click reaction was simply catalyzed by lithium hydroxide which proceeded readily at ambient conditions in very good yields. The incorporation of G-POSS into the network was clearly determined by transmission electron microscopy, FTIR, and 1H-NMR spectroscopy techniques performed with a model study using 1-butane thiol and G-POSS molecules. The homogeneous distribution of G-POSS up to 5 wt% in the hybrid network was apparently confirmed by morphological investigations. By increasing G-POSS content higher than 5 wt%, the heterogeneous dispersion of G-POSS was determined from the tensile strength measurements. The significant decrease in tensile strength was possible due to the agglomeration of G-POSS. On the other hand, thermal properties of hybrid networks were compared together by thermogravimetric analyses, where all samples exhibited one-step degradation in the range of 220–500 °C. The thermal decomposition of hybrid network led to complete degradation of the organic part and favored the formation of stable carbonaceous and inorganic residues as char. Thus, the char yields of hybrid networks were increased to 6.2, 7.8, 10.1, 12.7, and 15.1% by G-POSS loadings from 0 to 15 wt%. This improvement was also a proof of the incorporation of G-POSS into the hybrid networks that resulted in high heat-resistant POSS-based hybrid networks compared to a sample without G-POSS.
Open Access
Theoretical and spectroscopic investigations on the structure and bonding in B-C-N thin films
(2009) Bengu, E.; Genisel, M. F.; Gulseren, O.; Ovali, R.
In this study, we have synthesized boron, carbon, and nitrogen containing films using RF sputter deposition. We investigated the effects of deposition parameters on the chemical environment of boron, carbon, and nitrogen atoms inside the films. Techniques used for this purpose were grazing incidence reflectance-Fourier-transform infrared spectroscopy (GIR-FTIR), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM) and electron energy loss spectroscopy (EELS). GIR-FTIR experiments on the B-C-N films deposited indicated presence of multiple features in the 600 to 1700 cm- 1 range for the infrared (IR) spectra. Analysis of the IR spectra, XPS and the corresponding EELS data from the films has been done in a collective manner. The results from this study suggested even under nitrogen rich synthesis conditions carbon atoms in the B-C-N films prefer to be surrounded by other carbon atoms rather than boron and/or nitrogen. Furthermore, we have observed a similar behavior in the chemistry of B-C-N films deposited with increasing substrate bias conditions. In order to better understand these results, we have compared and evaluated the relative stability of various nearest-neighbor and structural configurations of carbon atoms in a single BN sheet using DFT calculations. These calculations also indicated that structures and configurations that increase the relative amount of C-C bonding with respect to B-C and/or C-N were energetically favorable than otherwise. As a conclusion, carbon tends to phase-segregate in to carbon clusters rather than displaying a homogeneous distribution for the films deposited in this study under the deposition conditions studied.