Browsing by Author "Sarkhosh H."
Now showing 1 - 3 of 3
Results Per Page
Sort Options
Item Open Access Evaluate of braze joint strength and microstructure characterize of titanium-CP with Ag-based filler alloy(2012) Ganjeh, E.; Sarkhosh H.; Khorsand H.; Sabet H.; Dehkordi, E.H.; Ghaffari, M.This research investigates the influences of brazing parameters (temperature and time) on microstructures and the mechanical properties of commercially pure (CP) titanium sheet when it is brazed with CBS34 (Ag-20Cu-22Zn-24Cd) braze filler foil. Brazing was performed in a conventional atmosphere control furnace. The brazing temperatures and holding times employed in this study were 800-870°C and 10-20min, respectively. The qualities of the brazed joints were evaluated by ultrasonic test and the microstructure and phase constitution of the bonded joints were analyzed by means of metallography, scanning electron microscope (SEM) and X-ray diffraction (XRD). The mechanical properties of brazed joints were evaluated by microhardness and shear tests. The diffusion between Ti, Ag, Cu, Zn and Cd from substrate and braze alloy, developed a strong reaction between each other. A number of intermetallic phases, such as TiCu and Ti2Cu in the Ag-Zn solid solution matrix have been identified especially at 870°C - 20min. Both the brazing temperature and the holding time are critical factors for controlling the microstructure and hence the mechanical properties of the brazed joints. The optimum brazing parameters was achieved at 870°C - 20min. Based on the shear test result, all cracks propagate along the brittle intermetallic compounds like Ti2Cu in the reaction layer which typically are composed of quasi-cleavage (Ag-Zn matrix) and brittle appearance. © 2012 Elsevier Ltd.Item Open Access Increasing Ti-6Al-4V brazed joint strength equal to the base metal by Ti and Zr amorphous filler alloys(2012) Ganjeh, E.; Sarkhosh H.; Bajgholi, M.E.; Khorsand H.; Ghaffari, M.Microstructural features developed along with mechanical properties in furnace brazing of Ti-6Al-4V alloy using STEMET 1228 (Ti-26.8Zr-13Ni-13.9Cu, wt.%) and STEMET 1406 (Zr-9.7Ti-12.4Ni-11.2Cu, wt.%) amorphous filler alloys. Brazing temperatures employed were 900-950 °C for the titanium-based filler and 900-990 °C for the zirconium-based filler alloys, respectively. The brazing time durations were 600, 1200 and 1800 s. The brazed joints were evaluated by ultrasonic test, and their microstructures and phase constitutions analyzed by metallography, scanning electron microscopy and X-ray diffraction analysis. Since microstructural evolution across the furnace brazed joints primarily depends on their alloying elements such as Cu, Ni and Zr along the joint. Accordingly, existence of Zr 2Cu, Ti 2Cu and (Ti,Zr) 2Ni intermetallic compounds was identified in the brazed joints. The chemical composition of segregation region in the center of brazed joints was identical to virgin filler alloy content which greatly deteriorated the shear strength of the joints. Adequate brazing time (1800 s) and/or temperature (950 °C for Ti-based and 990 °C for Zr-based) resulted in an acicular Widmanstätten microstructure throughout the entire joint section due to eutectoid reaction. This microstructure increased the shear strength of the brazed joints up to the Ti-6Al-4V tensile strength level. Consequently, Ti-6Al-4V can be furnace brazed by Ti and Zr base foils produced excellent joint strengths. © 2012 Elsevier Inc. All rights reserved.Item Open Access Investigation on braze joint strength and microstructure of Ti-CP with Ag and Ti base filler alloys(American Welding Society, 2012) Ganjeh, E.; Khorsand H.; Sarkhosh H.; Ghaffari, M.; Sabet H.; Dehkordi, E.H.This research investigates influences of brazing parameters (brazing alloy, temperature and time) on microstructures and mechanical properties of a commercially pure (CP) titanium sheet which is brazed with CBS 34 (Ag-based) and STEMET 1228 (Ti-based) braze-filler foils. Brazing was performed in a conventional inert furnace at temperature ranges of 800-870°C and 10-30 minutes for holding times. Qualities of the brazed joints were evaluated by ultrasonic testing, and then, microstructure and phase constitution of the bonded joints were analyzed by means of metallography, scanning electron microscope (SEM), and X-ray diffraction (XRD). Mechanical properties of brazed joints were evaluated by shear testing. Diffusion of titanium from substrate to filler alloy developed a strong reaction between them. A number of phases such as TiCu, Ti 2Cu, TiAg, Ag-Zn solid solution matrix (for Ag-based brazed samples) and Ti 2Cu, (Ti,Zr) 2Ni, Zr 2Cu (for Ti-based brazed samples) have been identified. The optimum brazing parameters were achieved at a temperature of 870 °C-20 min for CBS 34 and 870 °C-30 min for STEMET 1228. The specimen using STEMET 1228 braze alloy demonstrates best bonding strength (equal to Ti-CP tensile strength). Copyright 2012 ASM International® All rights reserved.