Browsing by Subject "Ideality factors"
Now showing 1 - 3 of 3
Results Per Page
Sort Options
Item Open Access Electrical characterization of MS and MIS structures on AlGaN/AlN/GaN heterostructures(ELSEVIER, 2010) Arslan, E.; Bütün, S.; Şafak, Y.; Uslu, H.; Tascioglu I.; Altindal, S.; Özbay, EkmelThe forward and reverse bias I-V, C-V, and G/ω-V characteristics of (Ni/Au) Schottky barrier diodes (SBDs) on the Al 0.22Ga 0.78N/AlN/GaN high-electron-mobility-transistor (HEMTs) without and with SiN x insulator layer were measured at room temperature in order to investigate the effects of the insulator layer (SiN x) on the main electrical parameters such as the ideality factor (n), zero-bias barrier height ( B0), series resistance (R s), interface-state density (N ss). The energy density distribution profiles of the N ss were obtained from the forward bias I-V characteristics by taking into account the voltage dependence of the effective barrier height ( e) and ideality factor (n V) of devices. In addition, the N ss as a function of E c-E ss was determined from the low-high frequency capacitance methods. It was found that the values of N ss and R s in SBD HEMTs decreases with increasing insulator layer thickness.Item Open Access Forward tunneling current in Pt/p-InGaN and Pt/n-InGaN Schottky barriers in a wide temperature range(Elsevier, 2012-07-27) Arslan, E.; Çakmak, H.; Özbay, EkmelThe current-transport mechanisms of the Pt contacts on p-InGaN and n-InGaN were investigated in a wide temperature range (80-360 K) and in the forward bias regime. It was found that the ideality factor (n) values and Schottky barrier heights (SBHs), as determined by thermionic emission (TE), were a strong function of temperature and Φb0 show the unusual behavior of increasing linearly with an increase in temperature from 80 to 360 K for both Schottky contacts. The tunneling saturation ( JTU(0)) and tunneling parameters (E 0) were calculated for both Schottky contacts. We observed a weak temperature dependence of the saturation current and a fairly small dependence on the temperature of the tunneling parameters in this temperature range. The results indicate that the dominant mechanism of the charge transport across the Pt/p-InGaN and Pt/n-InGaN Schottky contacts are electron tunneling to deep levels in the vicinity of mixed/screw dislocations in the temperature range of 80-360 K.Item Open Access Ta/Si Schottky diodes fabricated by magnetron sputtering technique(2010) Ocak, Y.S.; Genisel, M.F.; Kiliçoǧlu, T.Electrical properties of Ta/n-Si and Ta/p-Si Schottky barrier diodes obtained by sputtering of tantalum (Ta) metal on semiconductors have been investigated. The characteristic parameters of these contacts like barrier height, ideality factor and series resistance have been calculated using current voltage (I-V) measurements. It has seen that the diodes have ideality factors more than unity and the sum of their barrier heights is 1.21 eV which is higher than the band gap of the silicon (1.12 eV). The results have been attributed the effects of inhomogeneities at the interface of the devices and native oxide layer. In addition, the barrier height values determined using capacitance-voltage (C-V) measurements have been compared the ones obtained from I-V measurements. It has seen that the interface states have strong effects on electrical properties of the diodes such as C-V and Rs-V measurements. © 2010 Elsevier Ltd. All rights reserved.