Soylu, A. M.Polat, M.Erdogan, D. A.Say, Z.Yıldırım, C.Birer, Ö.Ozensoy, E.2016-02-082016-02-0820140169-4332http://hdl.handle.net/11693/26853TiO2-Al2O3 binary oxide surfaces were utilized in order to develop an alternative photocatalytic NOx abatement approach, where TiO2 sites were used for ambient photocatalytic oxidation of NO with O2 and alumina sites were exploited for NOx storage. Chemical, crystallographic and electronic structure of the TiO2-Al2O3 binary oxide surfaces were characterized (via BET surface area measurements, XRD, Raman spectroscopy and DR-UV-Vis Spectroscopy) as a function of the TiO2 loading in the mixture as well as the calcination temperature used in the synthesis protocol. 0.5 Ti/Al-900 photocatalyst showed remarkable photocatalytic NOx oxidation and storage performance, which was found to be much superior to that of a Degussa P25 industrial benchmark photocatalyst (i.e. 160% higher NOx storage and 55% lower NO2(g) release to the atmosphere). Our results indicate that the onset of the photocatalytic NOx abatement activity is concomitant to the switch between amorphous to a crystalline phase with an electronic band gap within 3.05-3.10 eV; where the most active photocatalyst revealed predominantly rutile phase together and anatase as the minority phase.EnglishAl2O3DeNOxNOx abatementPhotocatalysisTiO2Article10.1016/j.apsusc.2014.02.0651873-5584