Andonova, S. M.Şentürk, G. S.Kayhan, E.Ozensoy, E.2016-02-082016-02-0820091932-7447http://hdl.handle.net/11693/22717A ternary oxide-based NO* storage material in the form of BaOZTiO2Zy-Al2O3 was synthesized and characterized. Thermally induced structural changes occurring on the surfaces of the TiO2Zy-Al2O3 and BaOZ TiO 2Zy-Al2O3 systems were studied in a comparative manner within 300-1273 K via X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) spectroscopy, and BET surface area analysis. The surface acidity of the studied oxide systems was also investigated via pyridine adsorption monitored by in-situ Fourier transform infrared (FTIR) spectroscopy. BaO/TiO2γ-Al 2O3 ternary oxide was synthesized by incorporating different loadings of (8-20 wt %) BaO onto the TiO2/γ Al 2O3 support material, which was originally prepared using the sol-gel method. In the TiO2Zy-Al2O3 binary oxide support material, anatase phase exhibited a relatively high thermal stability at T < 1073 K. The presence of TiO2 domains on the surface of the alumina particles was found to alter the surface acidity of alumina by providing new medium-strength Lewis acid sites. SEMZEDX results indicate that in the BaO/TiO2γ-Al2O3 system, TiO2 domains present a significant affinity toward BaO and/or Ba(NO3) 2 resulting in a strong Ti-Ba interaction and the formation of overlapping domains on the surface. The presence of TiO2 also leads to a decrease in the decomposition temperature of the Ba(N03) 2 phase with respect to the Ti-free Ba(N03) 2ZyAl2O3 system. Such a destabilization is likely to occur due to a weaker interaction between Ba(N03) 2 and y-Al203 domains in the ternary oxide as well as due to the change in the surface acidity in the presence of TiO 2. At relatively high temperatures (e.g., 873-1273 K) formation of complex structures in the form of BaTiO3, Ba1.23Al 2.46Ti5.54O16, BaTiO5, andor Ba x:AlyTizOn., were also observed. © 2009 American Chemical Society.EnglishAlumina particlesAnatase phaseBET surface areaBinary oxidesComplex structureDecomposition temperatureEnergy dispersive x-rayHigh temperatureHigh thermal stabilityIn-situLewis acid siteOxide systemsPyridine adsorptionSEMSol-gel methodsStorage systemsStructural changeSupport materialsSurface acidityTernary oxidesThermally inducedTiOAdsorptionAluminumBariumFourier transform infrared spectroscopyGelationRaman spectroscopyScanning electron microscopySol-gel processSurface analysisSurfacesTitanium dioxideTitanium oxidesX ray diffractionX ray diffraction analysisBarium compoundsArticle10.1021/jp9005026