Browsing by Subject "Photoluminescence properties"

Now showing 1 - 3 of 3

Open Access
Bifunctional highly fluorescent hollow porous microspheres made of BaMoO4: Pr3+ nanocrystals via a template-free synthesis
(The Royal Society of Chemistry, 2011) Yang, X.; Zhou, Y.; Yu, X.; Demir, Hilmi Volkan; Sun, X. W.
We report a bifunctional hollow porous microsphere composed of single-component BaMoO4 : Pr3+ nanocrystals by a facile template-free synthesis. All the as-synthesized hollow microspheres are well-dispersed with a diameter of 2-4 mu m and the BaMoO4 : Pr3+ nanocrystals measure 30-60 nm in diameter. It is observed that there are a large amount of pores with an average diameter is 17.5 nm in the shell of these BaMoO4 : Pr3+ hollow microspheres, thereby exhibiting a great promise for drug delivery. Meanwhile, the strong, narrow-bandwidth red emission centered at 643 nm from these nanostructures can be efficiently excited from 430 nm to 500 nm. The combination of excellent luminescent properties and a hollow porous nanostructure suggest a great promise in the application of these nanostructures in lighting and displays, and in biomedicine such as targeted drug delivery, integrated imaging, diagnosis, and therapeutics. In addition, the template-free solution synthesis can be applied to the design and fabrication of other functional architectures.
Open Access
The effect of gadolinium doping on the structural, magnetic and photoluminescence properties of electrospun bismuth ferrite nanofibers
(Elsevier Ltd, 2015) George Philip G.; Senthamizhan, A.; Srinivasan Natarajan, T.; Chandrasekaran G.; Annal Therese H.
Gadolinium (Gd) doped Bismuth ferrite (BFO) nanofibers (Bi1-xGdxFeO3 (x=0.0, 0.05, 0.10, 0.15 and 0.20)) were synthesized via electrospinning. Scanning Electron Microscope (SEM) analysis showed that the diameter of the nanofibers ranged from 150 to 250 nm. X-Ray Diffraction (XRD) analysis revealed a structural phase transition with varying 'x', the compositions with x≤0.10 have crystal structures with space group R3c, while the compositions with x > 0.10 have crystal structures with space group Pnma. Vibrating Sample Magnetometer (VSM) analysis exhibited the weak ferromagnetic nature of the BFO nanofibers. However an increase in the saturated magnetic moment with increase in Gd dopant concentration was observed. The Photoluminescence (PL) spectra of the Bi:1-x :x nanofibers show enhanced Near Band Emission (NBE) intensity at x=0.10 due to the passivation of oxygen vacancies by Gd doping. © 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Open Access
Enhanced light scattering with energy downshifting using 16 nm indium nitride nanoparticles for improved thin-film a-Si N-i-P solar cells
(Electrochemical Society Inc., 2015-05) Chowdhury F.I.; İslam, K.; Alkış, Sabri; Ortaç, Bülend; Alevli, Mustafa; Dietz, N.; Okyay, Ali Kemal; Nayfeh, A.
In this work the effect of Indium nitride (InN) nanoparticles (NPs) on the performance of a-Si: H solar cells has been investigated. The average Jsc of InN NPs coated cells was found 6.76 mA/cm2 which is 16.69% higher than the average Jsc of the reference cell which was 5.79 mA/cm2. Average efficiency of InN NPs coated cells showed 14.16% increase from 3.32% to 3.79%. Peak EQE has increased from 44.8% at 500 nm to 51.67% at 510 nm and peak IQE has increased from 51.70% at 510 nm to 68.38% at 500 nm for InN NPs coated cell. Further study shows that EQE change is larger between 510 nm-700 nm compared to IQE change indicting a surface scattering mechanism that reduces the reflectivity. However, between 400 nm-510 nm IQE change is larger than EQE change which indicates that energy downshifting mechanism is dominating. So overall performance enhancement can be attributed to the scattering and photoluminescence properties of InN NPs that enhances absorption inside a-Si: H solar cells. © The Electrochemical Society.