Browsing by Subject "Adsorption capacities"
Now showing 1 - 2 of 2
- Results Per Page
- Sort Options
Item Open Access Direct evidence for the instability and deactivation of mixed-oxide systems: influence of surface segregation and subsurface diffusion(2011) Emmez, E.; Vovk, E. I.; Bukhtiyarov V. I.; Ozensoy, E.In the current contribution, we provide a direct demonstration of the thermally induced surface structural transformations of an alkaline-earth oxide/transition metal oxide interface that is detrimental to the essential catalytic functionality of such mixed-oxide systems toward particular reactants. The BaOx/TiO2/Pt(111) surface was chosen as a model interfacial system where the enrichment of the surface elemental composition with Ti atoms and the facile diffusion of Ba atoms into the underlying TiO2 matrix within 523 873 K leads to the formation of perovskite type surface species (BaTiO3/Ba2TiO4/BaxTiyOz). At elevated temperatures (T > 973 K), excessive surface segregation of Ti atoms results in an exclusively TiO2/TiOx-terminated surface which is almost free of Ba species. Although the freshly prepared BaOx/TiO2/Pt(111) surface can strongly adsorb ubiquitous catalytic adsorbates such as NO2 and CO2, a thermally deactivated surface at T > 973 K practically loses all of its NO2/CO2 adsorption capacity due to the deficiency of surface BaOx domains.Item Open Access Fabrication of cellulose acetate/polybenzoxazine cross-linked electrospun nanofibrous membrane for water treatment(Elsevier, 2017-12) Ertaş, Yelda; Uyar, TamerHerein, polybenzoxazine based cross-linked cellulose acetate nanofibrous membrane exhibiting enhanced thermal/mechanical properties and improved adsorption efficiency was successfully produced via electrospinning and thermal curing. Initially, suitable solution composition was determined by varying the amount of the benzoxazine (BA-a) resin, cellulose acetate (CA) and citric acid (CTR) to obtain uniform nanofibrous membrane via electrospinning. Subsequently, thermal curing was performed by step-wise at 150, 175, 200 and 225 °C to obtain cross-linked composite nanofibrous membranes. SEM images and solubility experiments demonstrated that most favorable result was obtained from the 10% (w/v) CA, 5% (w/v) BA-a and 1% (w/v) CTR composition and cross-linked nanofibrous membrane (CA10/PolyBA-a5/CTR1) was obtained after the thermal curing. Chemical structural changes (ring opening) occurred by thermal curing revealed successful cross-linking of BA-a in the composite nanofibrous membrane. Thermal, mechanical and adsorption performance of pristine CA and CA10/PolyBA-a5/CTR1 nanofibrous membranes were studied. Char yield of the pristine CA nanofibrous membrane has increased notably from 12 to 24.7% for composite CA10/PolyBA-a5/CTR1 membrane. When compared to pristine CA membrane, CA10/PolyBA-a5/CTR1 nanofibrous membrane has shown superior mechanical properties having tensile strength and Young's modulus of 8.64 ± 0.63 MPa and 213.87 ± 30.79 MPa, respectively. Finally, adsorption performance of pristine CA and CA10/PolyBA-a5/CTR1 nanofibrous membranes was examined by a model polycyclic aromatic hydrocarbon (PAH) compound (i.e. phenanthrene) in aqueous solution, in which CA10/PolyBA-a5/CTR1 nanofibrous membrane has shown better removal efficiency (98.5%) and adsorption capacity (592 μg/g).