Structural and microstructural phase evolution during mechano-synthesis of nanocrystalline/amorphous CuAlMn alloy powders
Okyay, A., K.
Please cite this item using this persistent URLhttp://hdl.handle.net/11693/20738
Advanced Powder Technology
- Research Paper 
The formation mechanism of Cu-11.5Al-4Mn alloys by mechanical alloying (MA) of pure elemental powders was investigated. During milling, the powder sampling was conducted at predetermined intervals from 1 h to 96 h. The quantitative phase analyses were done by X-ray diffraction and the particles size and morphology were studied by scanning electron microscopy. Furthermore, the microstructure investigation and phase identification were done by transmission electron microscopy. Concerning the results, the nanocrystalline Cu solid solution were formed at short milling times and, by milling evolution, the austenite-to-martensite (2H) phase transformation occurred. Moreover, the formation of considerable amount of amorphous phase and its partial transformation to crystalline phases during the milling process were revealed. It was also found that, by milling development, the powder morphology changes from lamellar to semi-spherical and their size initially increases, then reduces and afterward re-increases. © 2013 The Society of Powder Technology Japan. Published by Elsevier B.V. and The Society of Powder Technology Japan. All rights reserved.
Showing items related by title, author, creator and subject.
Amini, R.; Alijani F.; Ghaffari, M.; Alizadeh, M.; Okyay, A., K. (2012)Ti-41Ni-9Cu shape memory alloy was synthesized by mechanical alloying of pure elemental Ti, Ni, and Cu powders using high-energy ball milling. The qualitative and quantitative phase analyses of the as-milled powders were ...
Tolea, M.; Moldoveanu V.; Dinu I.V.; Tanatar, B. (2012)The usual experimental set-up for measuring the wave function phase shift of electrons tunneling through a quantum dot (QD) embedded in a ring (i.e., the transmittance phase) is the so-called 'open' interferometer as first ...
Structural, microstructural and thermal properties of lead-free bismuth-sodium-barium-titanate piezoceramics synthesized by mechanical alloying Amini, R.; Ghazanfari, M.R.; Alizadeh, M.; Ardakani H.A.; Ghaffari, M. (2013)Bismuth-sodium-barium-titanate piezoceramics with a composition of (Bi 0.5Na0.5)0.94Ba0.06TiO3 (BNBT) were prepared by mechanical alloying (MA). Structural analysis and phase identification were performed by X-ray diffraction ...